Optical fiber unit and optical fiber cable

ABSTRACT

An optical fiber unit includes: an optical fiber bundle formed by bundling a plurality of optical fibers; and a plurality of bundling members. One bundling member of the plurality of bundling members is wound on an outer circumference of the optical fiber bundle in a length direction of the optical fiber bundle, while reversing a winding direction alternately, and is joined to another bundling member at a section where the winding direction is reversed. A ratio of a width of a cross-section of the bundling member to a thickness of the cross-section of the bundling member is smaller than 20.

BACKGROUND

The present invention relates to an optical fiber unit and an opticalfiber cable.

Techniques are known for forming an optical fiber cable includingoptical fiber units which are optical fiber aggregates formed bybundling a plurality of optical fibers. In such techniques, it is commonto employ a method wherein a rough winding string (bundling member) iswound around the bundle of optical fibers to thereby suppress/preventthe bundle of optical fibers from falling apart while allowing theoptical fiber units to be differentiated from one another by the colorsof the bundling members.

In relation to such bundling members, particularly FIG. 7 of PatentLiterature 1 discloses a technique wherein the circumference of a bundleof a plurality of optical fibers is bundled with two bundling members bywinding the two bundling members in an S-Z configuration, and the twobundling members are bonded and fixed together at sections where theirwinding directions are reversed. Further, Patent Literature 2 disclosesa technique wherein three or more bundling members are provided tobundle a plurality of optical fibers, and a first bundling member isjoined to a second bundling member at a contact point where it contactsthe second bundling member, and is joined to a third bundling member ata contact point where it contacts the third bundling member, and awinding direction of a bundle of optical fibers is reversed at thecontact point to the second bundling member and the contact point to thethird bundling member.

CITATION LIST Patent Literature

Patent Literature 1: JP 2012-88454A

Patent Literature 2: WO2015/053146

SUMMARY

The optical fiber unit disclosed in Patent Literature 1 and PatentLiterature 2 has an advantage that workability when taking out anoptical fiber is improved. When winding a bundling member with a widthgreater than a thickness in a section of the bundling member in an S-Zconfiguration, however, the bundling member is twisted in sections wheretheir winding directions are reversed, and the bundling members may bejoined to each other in an upright form with respect to the opticalfiber bundle. There is a possibility that the optical fibers may breakbecause of the joined part of the bundling members that is upright inthis way gets entangled with another optical fiber bundle.

One or more embodiments of the present invention may suppress twists insections where winding directions of bundling members are reversed.

An aspect of the invention may include an optical fiber unit including:an optical fiber bundle formed by bundling a plurality of opticalfibers; and a plurality of bundling members, wherein one bundling memberof the plurality of bundling members is wound on an outer circumferenceof the optical fiber bundle in a length direction of the optical fiberbundle, while reversing a winding direction alternately, is joined toanother bundling member at a section where the winding direction isreversed, and a ratio of a width of a section of the bundling member toa thickness of the section of the bundling member is smaller than 20.

Other features of the present invention will be made clear by thefollowing description with reference to the drawings.

Advantageous Effects

According to one or more embodiments of the present invention, twist canbe suppressed in sections where winding directions of bundling membersare reversed.

BRIEF DESCRIPTION OF DRAWINGS

FIG. 1A is a sectional view of an optical fiber cable 1 including anoptical fiber unit 2. FIG. 1B is a perspective view of an optical fiberunit 2 of a Reference example.

FIG. 2 is an explanatory view of an optical fiber ribbon 7 withdiscontinuous connections.

FIG. 3 is a diagram illustrating a cross-sectional structure of abundling member 10 when joining by heat-sealing.

FIG. 4A to FIG. 4C are cross-sectional views of a bundling member 10explaining cross-sectional shapes of the bundling member 10.

FIG. 5 is an explanatory view explaining how to wind bundling members10.

FIG. 6 is a perspective view of a joined point 15 of bundling members 10enlarged in a comparative example.

FIG. 7 is a perspective view of a joined part of bundling members 10that is upright and joined in a section where winding directions ofbundling members are reversed.

FIG. 8 is a diagram explaining an optical fiber unit 2 in which anoptical fiber 8 has protruded out.

FIG. 9 is a diagram explaining an optical fiber unit 2 of a secondembodiment.

FIG. 10A is a developed view of bundling members 10 for explaining anexposed area of optical fibers. FIG. 10B is a developed view of otherbundling members 10 for explaining an exposed area of optical fibers.

DETAILED DESCRIPTION

At least the following matters are made clear from the followingdescription and the drawings.

An optical fiber unit will become clear including: an optical fiberbundle formed by bundling a plurality of optical fibers; and a pluralityof bundling members, wherein one bundling member of the plurality ofbundling members is wound on an outer circumference of the optical fiberbundle in a length direction of the optical fiber bundle, whilereversing a winding direction alternately, is joined to another bundlingmember at a section where the winding direction is reversed, and a ratioof a width of a section of the bundling member to a thickness of thesection of the bundling member is smaller than 20. According to such anoptical fiber unit, twist in sections where the winding direction of thebundling member is reversed can be suppressed.

A ratio of a width of a section of the bundling member to a thickness ofthe section of the bundling member may be equal to or smaller than 18.In this way, twist in sections where the winding direction of thebundling member is reversed can be suppressed.

The bundling members may be joined with an adhesive. It may beparticularly advantageous in such a case.

Where a number of the optical fibers is A, and a number of the bundlingmembers is N, an area in which the optical fiber is exposed from thebundling member on an outer circumference of the optical fiber bundlemay be equal to or smaller than 150 A/N mm². In this way, protruding outof optical fibers from a gap surrounded by the bundling members in thebending part of the optical fiber unit can be suppressed.

An area in which the optical fiber is exposed from the bundling memberon an outer circumference of the optical fiber bundle may be equal to orsmaller than 10 mm². In this way, the waterproof characteristic of thebundling members can be suppressed from deteriorating.

An optical fiber cable including: a plurality of optical fiber units;and an outer sheath for coating a plurality of the optical fiber units,wherein the optical fiber unit has an optical fiber bundle bundling aplurality of optical fibers, and a plurality of bundling members, onebundling member of the plurality of bundling members, is wound on anouter circumference of the optical fiber bundle along a length directionof the optical fiber bundle, while reversing alternately a windingdirection, is joined to another bundling member at a section where thewinding direction is reversed, and a ratio of a width of a section ofthe bundling member to a thickness of the section of the bundling membermay be smaller than 20. In this way, twist in sections where the windingdirection of the bundling member is reversed can be suppressed.

REFERENCE EXAMPLE

<Structure of Optical Fiber Unit 2 and the Like>

FIG. 1A is a sectional view of an optical fiber cable 1 includingoptical fiber units 2. The optical fiber cable 1 includes the pluralityof optical fiber units 2 and an outer sheath 3. The optical fiber unit 2is configured by bundling a plurality of optical fibers 8 with abundling member 10. A detailed configuration of the optical fiber unit 2will be described later. Here, the optical fiber cable 1 includes threeoptical fiber units 2. The three optical fiber units 2 are covered witha wrapping tape 5, and are coated on the outside with the outer sheath3. Tension members 4A and rip cords 4B are buried in the outer sheath 3.

FIG. 1B is a perspective view of the optical fiber unit 2 in a Referenceexample. The optical fiber unit 2 is configured by bundling a bundle ofa plurality of optical fibers 8 with a bundling member 10. Below, abundle of the plurality of optical fibers 8 is referred to as an opticalfiber bundle 6. The bundling member 10 is wound around on an outercircumference of the optical fiber bundle 6, and in this way theplurality of optical fibers 8 are bundled such that they do not fallapart. Here, the optical fiber bundle 6 bundles a plurality of opticalfiber ribbons 7 with discontinuous connections.

FIG. 2 is an explanatory view of an optical fiber ribbon 7 withdiscontinuous connections. The optical fiber ribbon 7 with discontinuousconnections is an optical fiber ribbon 7 in which a plurality of opticalfibers 8 are aligned and discontinuously connected. Here, twelve opticalfibers are aligned and connected. The adjacent two fibers of the opticalfibers 8 are connected with connection parts 9A. A plurality ofconnection parts 9A are arranged discontinuously in a length directionbetween adjacent two fibers of the optical fibers 8. The plurality ofconnection parts 9A of the optical fiber ribbon 7 with discontinuousconnections are arranged discontinuously two-dimensionally in the lengthdirection and a ribbon width direction. Regions other than theconnection parts 9A between adjacent two fibers of the optical fibers 8are non-connected parts 9B. In the non-connected parts 9B, adjacent twofibers of the optical fibers 8 are not tied to each other. Thus, theoptical fiber ribbon 7 with discontinuous connections can be rolled upinto a tubular shape (bundle shape), or can be folded up, thus enablingmultiple optical fibers 8 to be bundled at high density.

It should be noted that, the optical fiber ribbon 7 with discontinuousconnections configuring the optical fiber bundle 6 is not limited tothat shown in the diagram. For example, arrangement of the connectionparts 9A may be changed. Further, the number of the optical fibers 8configuring the optical fiber ribbon 7 with discontinuous connectionsmay be changed. Further, the optical fiber bundle 6 does not have to beconfigured with the optical fiber ribbon 7 with discontinuousconnections, and for example, may be configured by bundling theplurality of single fiber optical fibers 8.

The bundling member 10 is a member for bundling the plurality of theoptical fibers 8. The bundling member 10 is a string shaped, cordshaped, or ribbon shaped member that can tie the plurality of theoptical fibers 8. The bundling member 10 is wound around on an outercircumference of the optical fiber bundle 6. With the optical fiber unit2 in FIG. 1B, the optical fiber bundle 6 is bundled with four bundlingmembers 10, but the bundling members 10 around the optical fiber unit 2can be more than four. In the below description, an index (A-D) can beadded to the bundling member 10, to differentiate and describe eachbundling member 10.

The bundling members 10 are colored with predetermined colors, andfunction also as differentiating members. Each bundling member 10 ofeach optical fiber unit 2 is colored with a color different from eachother, and thus can be differentiated. As shown in FIG. 1B, in the casewhere each optical fiber unit 2 includes four bundling members 10,depending on the combination of colors of the bundling member 10, eachoptical fiber unit 2 can be differentiated. Further, instead of coloringthe bundling members 10, a differentiating mark may be printed on asurface of the bundling member 10.

The bundling members 10, for example, a bundling member 10(A) and abundling member 10(D), are joined, using an adhesive. As an adhesive forjoining the bundling members 10, for example, an adhesive such asmodified olefin having ultraviolet cure resin or a solvent, or areactive adhesive having such a component as an epoxy adhesive can beused. Further, the bundling members may be joined by heat-sealing, andnot by using an adhesive.

FIG. 3 is a diagram illustrating a cross-sectional structure of abundling member 10 when joined by heat-sealing. The bundling member 10has core parts 11 and a coating part 12. The core parts 11 are membersthat extend in the length direction of the optical fiber unit 2, and thebundling member 10 has a plurality of core parts 11. The coating part 12coats the periphery of the core parts 11, and is a member having a lowermelting point than a melting point of the core parts 11. The twobundling members 10 that bundle the optical fiber unit 2 are heat-sealedat intersections of the members, with adhesiveness that develops whenthe coating part 12 is heated to melting point or above. A differencebetween the melting point of the core part 11 and the melting point ofthe coating part 12 may be 20° C. or more. The melting point of the corepart 11 may be 200° C.-230° C., and the melting point of the coatingpart 12 may be 150° C.-180° C. Further, with the coating part 12, it maybe that even when the coating part is heated and melts it does notadhere to the optical fiber 8 nor has low adherence even when itadheres, and does not degrade the coating layer of the optical fiber 8.

FIG. 4A to FIG. 4C are sectional views of a bundling member 10 forexplaining sectional shapes of the bundling member 10. The sectionalshapes of the bundling member 10 can be various shapes. FIG. 4A shows acase where the sectional shape of the bundling member 10 is asubstantially square shape. FIG. 4B shows a case in which the sectionalshape of the bundling member 10 is shaped with the substantially squareshape in FIG. 4A rounded in the corner parts of the substantially squareshape. FIG. 4C shows a case where the sectional shape of the bundlingmember 10 is a substantially circular shape (includes an oval shape).

Next, parts which refer to a thickness and a width of each of the shapesare defined in this specification. In the sectional shapes shown in FIG.4A to FIG. 4C, the shortest part in cross section is referred to as athickness T, and the longest part that intersects the thicknessdirection is referred to as a width W. It should be noted that, FIG. 4Ato FIG. 4C show the case where the bundling member 10 is not upright andis wound around the optical fiber bundle 6, and the above-describeddefinition does not change even in the case where the bundling member 10is upright as will be described later.

FIG. 5 is an explanatory view explaining how to wind the bundlingmembers 10. Below, winding of the bundling member 10 around the opticalfiber bundle 6 is explained with reference to FIG. 1B.

The bundling member 10 is arranged such as to be wound on an outercircumference of the optical fiber bundle 6, in an arc shape for halfthe circumference (for 180 degrees) and along the length direction ofthe optical fiber unit 2. Then, the bundling member 10 is joined toanother bundling member 10 at the joined point 15. Further, the windingdirection of the bundling member 10 is reversed in respect to theoptical fiber bundle 6 at the joined point 15 with another bundlingmember 10. In this way, the bundling member 10 is wound around theoptical fiber bundle 6 in an S-Z configuration. It should be noted that,in the below description, an index AD is added to the joined point 15between the bundling member 10A and the bundling member 10D, and anindex BC is added to the joined point 15 between the bundling member 10Band the bundling member 10C, so that the joined points 15 can bedifferentiated in the explanation.

The bundling member 10 is wound on an outer circumference of the opticalfiber bundle 6 along the length direction of the optical fiber bundle 6,while reversing the winding direction alternately, and is joined toanother bundling member 10 in the section where the winding direction isreversed. In this way, when the joined point of the section in which thebundling member is reversed is separated, the bundling member 10 coatingthe periphery of the optical fiber bundle 6 in a net shape can beopened, and the optical fibers 8 can be taken out from the optical fiberunit 2.

The joining strength of the joined point 15 may be such that the joinedpoint 15 is not unintentionally destroyed, whereas the joined point 15can be easily separated with hands of an operator. A force necessary toseparate the joined point 15 of the bundling member 10 may be smallerthan a force required to cut the bundling member 10, and thus a joiningstrength of the bundling member 10 may be a breaking strength or less ofthe bundling member 10. Further, after the optical fiber 8 has beentaken out in mid-span branching, the two bundling members 10 may bejoined again by applying adhesive, or heating with a heater.

The joined points 15 are arranged so as to sandwich the optical fiberbundle 6, when the optical fiber unit 2 is seen from one side of thelength direction as shown in FIG. 5. Here for illustrative purposes, aposition of one joined point 15 is a reference position (0 degrees), anda position of the other joined point is at 180 degrees. In the Referenceexample, joined points 15AD and joined points 15BC are present in thereference position and in the position at 180 degrees.

First, winding of the bundling member 10A and the bundling member 10D ofthe four bundling members 10 is described. The bundling member 10A iswound clockwise on an outer circumference of the optical fiber bundle 6(see upper view in FIG. 5), is joined to the bundling member 10D atjoined point 15AD (see upper view in FIG. 5), is reversed in the windingdirection and is wound anticlockwise on an outer circumference of theoptical fiber bundle 6 (see center view in FIG. 5), joined to thebundling member D at joined point 15AD (see center view in FIG. 5),wound clockwise on an outer circumference of the optical fiber bundle 6again (see lower view in FIG. 5 (or upper view in FIG. 5)), and this isrepeated. Further, the bundling member 10A is wound anticlockwise on anouter circumference of the optical fiber bundle 6 (see upper view inFIG. 5), is joined to the bundling member 10A at joined point 15AD (seeupper view in FIG. 5), the winding direction is reversed and is woundclockwise on an outer circumference of the optical fiber bundle (seecenter view in FIG. 5), joined to the bundling member 10A at joinedpoint 15AD (see center view in FIG. 5), wound anticlockwise on an outercircumference of the optical fiber bundle 6 again (see lower view inFIG. 5 (or upper view in FIG. 5)), and this is repeated. In this way, asshown in FIG. 1B, the bundling member 10A and the bundling member 10Dare wound around the optical fiber bundle 6 in an S-Z configuration.Further, when seen from one side in the length direction of the opticalfiber unit 2 as shown in FIG. 5, two joined points 15AD are arranged soas to sandwich the optical fiber bundle 6 (joined points 15AD arearranged in positions at 0 degrees and 180 degrees).

The bundling member 10B and the bundling member 10C are similarly woundaround the optical fiber bundle 6 in an S-Z configuration, as shown inFIG. 1B. Two joined points 15BC are arranged so as to sandwich theoptical fiber bundle 6 (joined points 15BC are arranged at positions of0 degrees and 180 degrees) when viewed from one side in the lengthdirection of the optical fiber unit 2 as shown in FIG. 5.

<Twist of Bundling Member 10 in Section where Direction is Reversed>

FIG. 6 is an enlarged perspective view showing a part near a joinedpoint 15 of bundling members 10 of a comparative example. It should benoted that, only the bundling members 10 are shown in FIG. 6 to make thedescription easier to understand, and the optical fiber bundle 6 is notshown. As shown in FIG. 6, the bundling member 10 that has been woundaround in an S-Z configuration is reversed in the winding direction at ajoined point 15 with another bundling member 10. When the windingdirection of the bundling member 10 is reversed, bending stress M iscaused in the bundling member 10. The bending stress M is a generic termfor two stresses of a compressive stress in an inner side of the bendand a tensile stress to an outer side of the bend, with a center line ofthe bundling member 10 as a reference as shown by a broken line in FIG.6.

By the way, the bending stress that generally develops in a member isknown to vary depending on the sectional shape. In other words, theflexibility of the member depends on the sectional shape. Further, it isgenerally known that a member having the sectional shape with athickness and a width that are different from each other such as arectangle, has varying flexibility depending on the ratio of the widthto the thickness. When the bundling member 10 shown in FIG. 6 is to bebent in the width direction, the greater the width W with respect to thethickness T the harder it becomes to bend. When the bundling member 10with the width W of a certain amount or greater with respect to thethickness T is to be bent in the width direction, there is a possibilitythat the stress cannot be borne with only bending deformation of themember. At this time, the compressive stress and the tensile stressaffect the direction of the twist, as a result there is a case where thebundling member 10 twists and deforms.

FIG. 7 is a perspective view of a joined part of the bundling members 10that are upright and joined in a section where winding directions ofbundling members are reversed. In the case where the compressive stressaffects the upright direction with respect to the optical fiber bundle6, and the tensile stress affects the length direction of the opticalfiber bundle 6, the bundling members 10 are twisted, and as a result thesection where the bundling member 10 is reversed stands and is joined.The joined parts of the bundling members 10 that are upright in this wayentangle with optical fibers of other optical fiber bundles 6, tolargely bend the optical fiber locally, and to possibly cause increaseof transmission loss. Further, there is a possibility of breaking theoptical fibers that have been entangled.

First Embodiment

(Evaluation of Characteristic of Entanglement Caused by Bundling MemberJoined Part)

Entanglement of an optical fiber caused by the joined part of thebundling members 10 occurs when the joined part of the bundling membersare upright in the case where the width W is equal to or greater than acertain amount with respect to the thickness T of the bundling member. Aplurality of prototype optical fiber units were formed in respect to thesection size of the bundling member, to evaluate the characteristic ofentanglement caused by the joined part of the bundling members 10.

First, the plurality of the prototype optical fiber units each has 80optical fibers that are aggregated, and is wound with the bundlingmember in an S-Z configuration. The wrapping method of the bundlingmember is the same as that shown in FIG. 1B and FIG. 5. The plurality ofprototype optical fiber units with varying widths and thicknesses areformed, are each rotated, and it was evaluated whether or not the joinedpart of the bundling members of the prototype optical fiber unit isentangled in the optical fiber bundle of the other optical fiber unit,when contacted to the other optical fiber unit. The evaluation result isas shown in Table 1 below.

TABLE 1 THICKNESS OF BUNDLING MEMBER [mm] 0.02 0.04 0.06 0.08 0.10 0.120.14 0.16 WIDTH OF 0.20 10.0  5.0  3.3  2.5  2.0  1.7 1.4 1.3 BUNDLING ✓✓ ✓ ✓ ✓ ✓ ✓ ✓ MEMBER 0.40 20.0 10.0  6.7  5.0  4.0  3.3 2.9 2.5 [mm] x ✓✓ ✓ ✓ ✓ ✓ ✓ 0.60 30.0 15.0 10.0  7.5  6.0  5.0 4.3 3.8 x ✓ ✓ ✓ ✓ ✓ ✓ ✓0.80 40.0 20.0 13.3 10.0  8.0  6.7 5.7 5.0 x x ✓ ✓ ✓ ✓ ✓ ✓ 1.00 50.025.0 16.7 12.5 10.0  8.3 7.1 6.3 x x ✓ ✓ ✓ ✓ ✓ ✓ 1.20 60.0 30.0 20.015.0 12.0 10.0 8.6 7.5 x x x ✓ ✓ ✓ ✓ ✓ 1.40 70.0 35.0 23.3 17.5 14.011.7 10.0  8.8 x x x ✓ ✓ ✓ ✓ ✓ 1.60 80.0 40.0 26.7 20.0 16.0 13.3 11.4 10.0  x x x x ✓ ✓ ✓ ✓ 1.80 90.0 45.0 30.0 22.5 18.0 15.0 12.9  11.3  x xx x ✓ ✓ ✓ ✓ 2.00 100.0  50.0 33.3 25.0 20.0 16.7 14.3  12.5  x x x x x ✓✓ ✓

In Table 1, the upper row of each evaluation result field shows a ratioof a width of a bundling member to a thickness of a bundling member.Below, this ratio is referred to as a width-thickness ratio. In thelower row of the evaluation result field, when the prototype opticalfiber unit is made to contact another optical fiber unit and the joinedpart does not get entangled in rotation it is shown by “√”, and when thejoined part gets entangled in rotation it is shown by “×”. When theresult is “√”, the optical fiber unit can be evaluated as a satisfactoryoptical fiber unit in which the joined part being upright is suppressedsuch that entanglement of an optical fiber caused by the joined part ofthe bundling members does not occur.

As is clear from the results shown in Table 1, the prototype opticalfiber units with a width-thickness ratio of less than 20.0 are evaluatedas “√”. Of the prototype optical fiber units evaluated as “√”, theprototype optical fiber unit with the greatest width-thickness ratio hasa width of 1.80 mm, a thickness of 0.10 mm, and a width-thickness ratioof 18.0. Thus, from the above results, the optical fiber unit with thewidth-thickness ratio of smaller than 20.0, may be equal to or smallerthan 18.0, is a satisfactory optical fiber unit in which the joined partbeing upright is suppressed such that entanglement of an optical fibercaused by the joined part of the bundling members does not occur.

(How Twist Occurs Depending on Joining Method of Bundling Member)

Joining of the bundling members 10 is carried out using an adhesive orby heat-sealing. Of these cases, compared to heat-sealing, twist easilyoccurs in the bundling member in the section where the winding directionis reversed when joining with an adhesive. This is because inheat-sealing the coating part 12 (see FIG. 3) of the bundling member 10melts and becomes slight easily deformable, thus the bundling member 10becomes more easy to bend. Thus, the optical fiber unit with theabove-described numerical range is particularly advantageous whenjoining with an adhesive.

Second Embodiment

<Protruding Out of Optical Fiber>

In the above-described Reference example, when the optical fiber unit isbent, an optical fiber may protrude out from a gap surrounded with thebundling members. When this protruded out portion of the optical fibergets entangled in another optical fiber unit, or gets entangled in thebundling member, local bending of the optical fiber causes transmissionloss increase and breakage of optical fibers.

FIG. 8 is a diagram explaining an optical fiber unit 2 in which anoptical fiber 8 has protruded out. Note that, to make explanationsimpler in FIG. 8, only one of the plurality of bundling members 10 isshown, and other bundling members 10 that are to be joined to thisbundling member are not shown. In the below description, indexes (A, B)are added to the optical fibers 8. As shown in FIG. 8, when the opticalfiber unit 2 is bent, a difference in line length arises between thepaths of the optical fibers 8 from an S point to an E point. Forexample, the length of the path of an optical fiber 8(A) that passes aninner side of the bend becomes shorter than the length of the path of anoptical fiber 8(B) that passes an outer side of the bend.

As the optical fiber 8(A) is wound with the bundling member 10 and istied, however, the optical fiber 8(A) actually passes a path to resolvethe difference in line length with the optical fiber 8(B). In otherwords, the optical fiber 8(A) accumulates the difference in line lengthby winding, to try to resolve the difference in line length with theoptical fiber 8(B). But, when the optical fiber bundle is wound around adrum and the like so as to be bent continuously, the difference in linelength cannot be resolved merely with winding, and after a certainamount of accumulation of the difference in line length, an opticalfiber finally protrudes out from a gap surrounded with the bundlingmembers 10.

<Exposed Area of Optical Fiber>

FIG. 9 is a diagram explaining an optical fiber unit 2 of a secondembodiment. As shown in FIG. 9, by increasing the number of bundlingmembers and making a pitch of winding of the bundling member short, theprotruding out of the optical fiber 2 can be suppressed. This is becausethe portion where the bundling member 10 is not wound around, that is anarea where the optical fibers are exposed becomes smaller, and as aresult protruding out of the optical fiber 2 can be suppressed.

FIG. 10A is a developed view of bundling members 10 explaining anexposed area of optical fibers. FIG. 10A shows a peripheral surface ofthe optical fiber bundle 6 virtually as a circumferential surface, andshows the bundling members 10 wound on an outer circumference of theoptical fiber bundle 6 unfolded. The bundling member 10 is wound on theouter circumference of the optical fiber bundle 6 while reversing thewinding direction alternately along the length direction thereof, and isjoined to another bundling member 10 in a section in which the windingdirection is reversed. An exposed area in this example, is an area of aregion surrounded with bundling members as shown by a shaded part inFIG. 10A.

FIG. 10B is a developed view of other bundling members 10 for explainingan exposed area of optical fibers. In FIG. 10B four bundling members 10are arranged, and the bundling members 10 are joined not only insections in which the winding direction is reversed, but also atintersections where the bundling members intersect with other bundlingmembers 10. The exposed area in this example is an area of a regionsurrounded with bundling members shown by a shaded part in FIG. 10B.

<Evaluation of Protruding Characteristic of Optical Fiber>

Protruding out of an optical fiber is caused when an exposed area is acertain area or greater. A plurality of prototype optical fiber unitswere made with respect to exposed areas, and a protruding characteristicof an optical fiber was evaluated.

First, an optical fiber bundle having 8 fiber ribbons with discontinuousconnections for a total of 80 fibers, and a bundling member with athickness of 0.08 mm and a width of 1.4 mm were prepared. A plurality ofprototype optical fiber units were formed in which the winding pitch ofthe bundling member has been changed to thus change the exposed area, inrespect to bundling members that have been changed in number from two toeight. The prototype optical fiber units were bent, to evaluate whetheror not the optical fiber protrudes out. The evaluation results are asshown in Table 2 below.

TABLE 2 NUMBER OF BUNDLING MEMBERS [NUMBER] 2 3 4 5 6 7 8 EXPOSED 3 ✓ ✓✓ ✓ ✓ ✓ ✓ AREA 5 ✓ ✓ ✓ ✓ ✓ ✓ ✓ [mm²] 10 ✓ ✓ ✓ ✓ ✓ ✓ ✓ 20 ✓ ✓ ✓ ✓ ✓ ✓ ✓30 ✓ ✓ ✓ ✓ ✓ ✓ ✓ 50 ✓ ✓ ✓ ✓ ✓ ✓ ✓ 75 ✓ ✓ ✓ ✓ ✓ ✓ ✓ 100 ✓ ✓ ✓ ✓ ✓ ✓ ✓ 150✓ ✓ ✓ ✓ ✓ ✓ x 200 ✓ ✓ ✓ ✓ ✓ x x 250 ✓ ✓ ✓ ✓ x x x 300 ✓ ✓ ✓ x x x x 400✓ ✓ x x x x x 500 ✓ x x x x x x 600 ✓ x x x x x x 700 x x x x x x x

In Table 2, an evaluation result field in which the optical fiber hasnot protruded out is shown as “√”, and an evaluation result field inwhich the optical fiber has protruded out is shown as “×”. If the resultis “√”, the optical fiber unit can be evaluated as being a satisfactoryoptical fiber unit in which the optical fiber does not protrude out evenwhen the optical fiber unit is bent.

From the results of Table 2, the below equation 1 can be shown with anexposed area as S (mm²), and the number of bundling members as N(number).[Number 1]S≤1200/N  (Equation 1)

Further, whether or not protruding out occurs when using a singleoptical fiber with 1 fiber was also evaluated. The evaluation resultsare as shown in Table 3 below.

From the results of Table 2 and Table 3, conditions for an exposed areaS for one optical fiber can be obtained. The following Equation 2 isshown with an exposed area as S (square mm), the number of bundlingmembers as N (number), number of fibers per one optical fiber (includinga ribbon) as A.[Number 2]S≤150A/N  (Equation 2)

TABLE 3 NUMBER OF BUNDLING MEMBERS [NUMBER] 2 3 4 5 6 7 8 EXPOSED 3 ✓ ✓✓ ✓ ✓ ✓ ✓ AREA 5 ✓ ✓ ✓ ✓ ✓ ✓ ✓ [mm²] 10 ✓ ✓ ✓ ✓ ✓ ✓ ✓ 20 ✓ ✓ ✓ ✓ ✓ x x30 ✓ ✓ ✓ ✓ x x x 50 ✓ ✓ x x x x x 75 ✓ x x x x x x 100 x x x x x x x 150x x x x x x x 200 x x x x x x x 250 x x x x x x x 300 x x x x x x x 400x x x x x x x 500 x x x x x x x 600 x x x x x x x 700 x x x x x x x

<Evaluation of Waterproof Characteristic>

Depending on the application environment of the optical fiber cable,water may infiltrate into the optical fiber cable. The infiltrated waterreaches a junction box such as a closure through the optical fibercable, and there is a possibility that the water may affect otheroptical fiber cables via the junction box. Thus, the optical fiber cableneeds to have satisfactory waterproof characteristic. Generally,waterproof performance inside the optical fiber unit is increased byapplying a waterproof material to a surface of the wrapping tape 5facing the optical fiber unit shown in FIG. 1A. At this time, when thearea of the region surrounded by the bundling members, namely theexposed area, is smaller than a certain value, the waterproof materialis blocked with the bundling members and does not spread over the insideof the optical fiber unit. As a result, the waterproof characteristicmay deteriorate.

The waterproof characteristic of the above prototype optical fiber cablewas evaluated. The evaluation was carried out with the prototype opticalfiber cable length as 40 m, water being injected from an end face of anoptical fiber cable with water head length of 1 m, and with a test timeof 240 hours. As the water for the evaluation, artificial seawater with24.5 g of sodium chloride and 11.1 g of magnesium chloride hexahydratedissolved per 1 liter of water was used. The evaluation results are asshown in Table 4 below.

TABLE 4 NUMBER OF BUNDLING MEMBERS [NUMBER] 2 3 4 5 6 7 8 EXPOSED 3 x xx x x x x AREA 5 x x x x x x x [mm²] 10 ✓ ✓ ✓ ✓ ✓ ✓ ✓ 20 ✓ ✓ ✓ ✓ ✓ ✓ ✓

From the results in Table 4, the waterproof performance does not dependon the number of the bundling members, and by making an exposed area 10square mm or greater, sufficient effect was achieved.

From the results of Table 2 to Table 4, an upper limit and a lower limitof the exposed area S for one optical fiber can be obtained. Theequation is below Equation 3 as shown with an exposed area as S (squaremm), the number of bundling members as N (number), and the number forone optical fiber (including ribbon) as A.[Number 3]10≤S≤150A/N  (Equation 3)

Other Embodiment

The foregoing embodiments are for facilitating the understanding of thepresent invention, and are not to be construed as limiting the presentinvention. The present invention may be modified and/or improved withoutdeparting from the gist thereof, and it goes without saying that thepresent invention encompasses any equivalents thereof.

<Number of Bundling Members 10>

The foregoing embodiment describes an example in which there are fourbundling members 10 wound on the optical fiber bundle 6. However, thenumber of bundling members 10 to be provided in a single optical fiberunit 2 is not limited thereto. For example, there may be six or morebundling members, or an odd number of bundling members.

Although the disclosure has been described with respect to only alimited number of embodiments, those skilled in the art, having benefitof this disclosure, will appreciate that various other embodiments maybe devised without departing from the scope of the present invention.Accordingly, the scope of the invention should be limited only by theattached claims

REFERENCE SIGNS LIST

-   1 optical fiber cable, 2 optical fiber unit, 3 outer sheath,-   4A tension member, 4B rip cord, 5 wrapping tape,-   6 optical fiber bundle, 7 optical fiber ribbon with discontinuous    connections,-   8 optical fiber, 9A connection part, 9B non-connected part,-   10 bundling member,-   15 joined part

The invention claimed is:
 1. An optical fiber unit comprising: anoptical fiber bundle formed by bundling a plurality of optical fibers;and a plurality of bundling members, wherein one bundling member of theplurality of bundling members: is wound on an outer circumference of theoptical fiber bundle in a length direction of the optical fiber bundle,while reversing a winding direction alternately, and is joined toanother bundling member at a section where the winding direction isreversed, wherein a ratio of a width of a cross-section of the bundlingmember to a thickness of the cross-section of the bundling member issmaller than
 20. 2. The optical fiber unit according to claim 1, whereinthe ratio of a width of the cross-section of the bundling member to thethickness of the cross-section of the bundling member is equal to orsmaller than
 18. 3. The optical fiber unit according to claim 1, whereinthe bundling members are joined with an adhesive.
 4. The optical fiberunit according to claim 1, wherein an area in which the optical fiber isexposed from the bundling member on the outer circumference of theoptical fiber bundle is equal to or smaller than 150A/N mm², where A isa number of the optical fibers, and N is a number of the bundlingmembers.
 5. The optical fiber unit according to claim 4, wherein thearea in which the optical fiber is exposed from the bundling member onthe outer circumference of the optical fiber bundle is equal to orsmaller than 10 mm².
 6. An optical fiber cable comprising: a pluralityof optical fiber units; and an outer sheath that coats a plurality ofthe optical fiber units, wherein the optical fiber unit comprises: anoptical fiber bundle bundling a plurality of optical fibers; and aplurality of bundling members, one bundling member of the plurality ofbundling members: is wound on an outer circumference of the opticalfiber bundle along a length direction of the optical fiber bundle, whilereversing alternately a winding direction, and is joined to anotherbundling member at a section where the winding direction is reversed,wherein a ratio of a width of a cross-section of the bundling member toa thickness of cross-section of the bundling member is smaller than 20.7. An optical fiber unit comprising: an optical fiber bundle formed bybundling a plurality of optical fibers; and a plurality of bundlingmembers, wherein a first bundling member of the plurality of bundlingmembers: is wound on an outer circumference of the optical fiber bundlein a length direction of the optical fiber bundle, while reversing awinding direction alternately, and is joined to a second bundling memberat a section where the winding direction is reversed, wherein a thirdbundling member of the plurality of bundling members: is wound on anouter circumference of the optical fiber bundle in a length direction ofthe optical fiber bundle, while reversing a winding directionalternately, and is joined to a fourth bundling member at a sectionwhere the winding direction is reversed, wherein the first bundlingmember and the third bundling member form a first intersection and arejoined at the first intersection, and the second bundling member and thefourth bundling member form a second intersection and are joined at thesecond intersection, wherein a ratio of a width of a cross-section ofeach bundling member to a thickness of the cross-section of the samebundling member is smaller than 20, and wherein an area in which theoptical fiber is exposed from the bundling member on the outercircumference of the optical fiber bundle is equal to or smaller than150A/N mm², where A is a number of the optical fibers, and N is a numberof the bundling members.
 8. The optical fiber unit according to claim 1,wherein the ratio of the width of the cross-section of the bundlingmember to the thickness of the cross-section of the bundling member isequal to or greater than 1.3.